ABS 3.0 Photopolymer Resin (405nm & 1KG)

ELEGOO ABS-Like Resin 3.0 was developed for those who need high strength, durability, and precision in 3D printing . With an optimized formula for less shrinkage and greater toughness , this resin is perfect for parts that require robustness, such as functional prototypes, mechanical components, and industrial applications .

Its enhanced fluidity ensures rapid prototyping, with efficient curing and less printing time, as well as a better success rate. Another advantage is its strong stability , which prevents delamination or separation of the resin over time, always maintaining uniform colors and consistency in the models.

Main Features

• High strength and toughness : withstands impacts and mechanical loads without losing structural integrity.
• High precision with low shrinkage : models with sharp details, dimensional stability, and smooth surfaces.
• Good flowability for rapid prototyping : reduced viscosity (25-47% lower than previous versions), resulting in faster and more successful prints.
• Enhanced stability : resin does not delaminate over time, ensuring color consistency and print quality.
• Wide compatibility : works on 405nm UV LCD/DLP printers, with optimal performance on ELEGOO printers.

Technical Specifications

• Product: ELEGOO ABS-Like Resin 3.0
• Volume: 1KG
• Type: Light-cured (UV) resin
• Healing wavelength: 385nm – 410nm (optimal at 405nm)
• Tensile strength: 40 ±10% MPa
• Deformation at the point of maximum force: 15.18 ±10% mm
• Elongation at the memory point: 5.77 ±10%
• Elongation at break: 24 ±10%
• Maximum flexural strength: 50 ±10% MPa
• Flexible modulus: 1200 ±10% MPa
• Hardness (Shore D): 80 – 88D
• Impact force: 72.4 ±10% J/m
• Tensile modulus: 480.63 ±10% MPa
• Viscosity: 180 – 210 MPa·sa 25°C
• Density: 1.05 – 1.25 g/cm³ at 25°C
• Volume shrinkage: 0.2% – 0.7%
• Form: Photosensitive liquid
• Shelf life: 2 years
• Origin: China (ELEGOO)

Compatible with LCD and DLP printers that use 405nm UV , ABS 3.0 resin offers superior performance compared to previous versions (ABS 1.0 and 2.0), featuring up to 47% reduced viscosity, resulting in better flow and finish.